Aqueous Hydroxyl Functional Acrylic Resin Excellent Impact Resistance Good Gloss

Basic Information
Place of Origin: china
Brand Name: WeiLi Resin®
Certification: ISO9001
Model Number: WL-H152
Minimum Order Quantity: 5000KG
Price: Negotiable
Packaging Details: 200kg/drum
Delivery Time: 14 work days
Payment Terms: L/C, T/T
Supply Ability: 500t/month
Detail Information
Appearance: Milky White Liquid Non-volatile Matters(%): 43±2
Viscosity (mPa*s): ≤500 PH: 7.0-8.0
VOC(%): <5 Hydroxyl Value (mgKOH/g): 108
Density(g/cm3): 1.047 Package: 200kg
High Light:

two part acrylic resin

,

acrylic resins for coatings

,

Aqueous Hydroxyl Functional Acrylic Resin


Product Description

Water based hydroxyl functional acrylic WL-H152

 

Water Dispersion Hydroxyl Acrylic ResinWL-H152 is two component PU resin, it is suggested to be used cooperatively with poly aliphatic isocyanate curing agent, through baking, it can maximize performance.water based hydroxyl acrylic dispersion can produce the same hardness, impact resistance and solvent resistance as solvent based polyurethane coating. PU coating made of WL-H152 is recommended to use in topcoat of metal or wood due to its paint film has excellent gloss, the construction method can be brushing, roll coating or spraying.

 

 

1, Product Composition:

Waterborne hydroxyl Acrylic Dispersion, Cosolvent, Neutralizing Agent, Water

 

2, Typical Data:

 

Item WL-H152 Test Method
Appearance Milky White Liquid Visual Observation
Non-volatile Matters(%) 43±2 30min@120℃
Viscosity (mPa*s) ≤500 Rotational Viscometer
pH 7.0-8.0 PH Meter
VOC(%) <5  
Hydroxyl Value (mgKOH/g) 108 (For solid resin, theoretical value)
Density(g/cm3) 1.047 Densimeter

 

3, Product Properties:

Self emulsifying process, emulsifier free.

Excellent shear stability, can be grinded with dispersions directly.

Good gloss, hardness and limit film thickness.

Excellent weather resistance, water resistance and aging resistance.

 

4, Instructions:

WL-152 can be diluted with deionized water to construction viscosity. The resin can help to wet pigments, so wetting agent may reduce PH valueof the coating system can always be adjusted by N. N-dimthylethanolamine, viscosity of the dispersion will increase as the PH value increases

WL-152 can be mixed with poly aliphatic isocyanate curing agent for preparing high-gloss top coating which can dry fast at room temperature ordry by force at 80"C. The activation period is about 3 hours if it is used with BAYHYDUR 304(NCO/OH=1. 4/1.0).

Construction equipments can be cleaned by water, alkaline detergent or water soluble solvent.

5, Product Properties Test:

Gloss(60o)high gloss kind >90 Adhesion(grid) 0 grade
Surface dry min(23o) 15min Adhesion(circle) 1grade
Air dry 25o/h 4h Water resistance(23o) 480h
Baking 65o/min 65o,30min

Alkaline resistance

(25o 0.1N NaOH)

24h
Pot life(25o) 4h

Acid resistance

(25o 0.1N H2SO4)

24h
Hardness(pencil) 1H-2H Gasoline resistance 24h
Flexibility/mm 1grade Artificial aging resistance

1000h

Loss of gloss 30%

Impact resistance kg*cm 50 Q-sun,1200h 1grade
Heat resistance 105o Continue 24h 24h

 

 

6, Storage:

It is suggested that the product should be stored in a cool and dry weak alkaline place. The quality guarantee period is 6 months, and the expiredproducts can still be used after passing the inspections.

7, Applications:

2KPU self-drying top coatings and amino-baking top coatings.

8, Note:

the specification is a general introduction to the products of our company. It will be adjusted with the product improvement Please contact with thecompany to obtain the latest product description.